Название On the use of silicon for production of quality welded brass tubes
DOI 10.17580/tsm.2023.02.11
Автор Pevzner M. Z.
Информация об авторе

Vyatka State University, Kirov, Russia:

M. Z. Pevzner, Professor, e-mail: mikhailpevzner@yandex.ru

Реферат

This paper looks at the effect of Si impurity combined with Pb impurity, as well as that of structural and process factors on the quality of high-frequency continuous tube welding. The aim of this research is to check the effectiveness of silicon alloying and develop the most efficient process for making bands to be used in high-frequency welding by determining an optimum silicon alloying degree. The paper describes the results of passive and active-passive field experiments, which imply that some of the parameters conform to the conventional production process and some vary. Such variation may be random, associated with the changing chemical composition of the burden, or it may be intentional. Scrap of silicon-bearing alloy LK75-0.5 was used as one of the burden components or pure Si was introduced when smelting L68 brass in ILK-1.6 furnaces. As a result, the concentration of silicon varied between 0.003 and 0.480% Si. First, the composition of sample castings was monitored with the help of rapid spectral analysis. At the final stage, the authors looked at the composition of ingots by examining the cut-off corners of the samples. The ingots were heated to 800–840 oC, and those containing 0.1% Si were heated separately to the upper values of this range. After the ingots had been hot rolled down to 5.5 mm and the resultant strips – subjected to double-sided milling, they were taken through a three-stand mill and in two passes rolled down to an interim thickness of 3.2 mm and then to a final thickness of 1.4–1.6 mm. Some batches were annealed when the band was 3.2 mm thick (k = 2), some — not (k = 1). At the intermediate annealing stage, the temperature of 620 ± 10 oC was applied for 5 hours. The final annealing stage was based on a varying temperature mode, with the grain size reached being μ = 15–130 μm. The forming and high-frequency welding of brass tubes were performed in a tube electric-welding plant TESA 15-50 in the following regime: frequency — 440 kHz, speed — 59–60 m/min, anode voltage — 10–11 kV, oscillating circuit current — 0.85–0.95 MA, grid current — 4.8 А, anode current — 16 A. Drift and flattening tests were conducted for the welded tubes; the chemical composition and structure were monitored; the tubes were subjected to drawing and a final hydrological highpressure test. The welding quality assessment was based on a 1-5-point system. It was found that the grain size μ, the band thickness h and the Pb concentration affect the product quality, while Si (with confidence >99.99%) and the number of transitions during rolling — k produce a positive effect. With any combination of the other factors, the concentration 0.1–0.3% Si and μ ≤ 100 μm would ensure the welding quality of 5 points. However, such high concentration of Si caused serious production problems entailing a risk of compromised chemical composition or mechanical properties. In order to lower the required amount of Si by setting limits for other process parameters, the following parameters were additionally played with: h, Pb and k. The obtained results formed the basis for developing certain process (h ≤ 1.4 mm; k ≥ 2; μ ≤ 50 μm) and chemical (0.05–0.1% Si, Pb ≤ 0.018%) limits. Introduction of the above limits helped reach the welding quality of 5 points.

Ключевые слова Tube production, heat exchangers, brass tubes, high-frequency welding, tube welding quality, composition of L68 brass, concentration of impurities, silicon alloying
Библиографический список

1. Mishra S., Sharma S. K., Kumar S., Sagar K. et al. 40 kJ magnetic pulse welding system for expansion welding of aluminium 6061 tube. Journal of Materials Processing Technology. 2017. Vol. 240. pp. 168–175.
2. Miao G., Li S.-X., Lu F., Liu Y.-J., Yang L.-M. Manufacture of brass tube bundles of heat exchangers. Petrochemical Equipment. 2017. Vol. 46, Iss. 3. pp. 31–35.
3. Kazano W., Beszak B., Karbownik A. Copper and brass tubes from strip. Tube International. 1989. Vol. 8, No. 2. pp. 90–92, 94.
4. Saluja R. S., Singh V. MADM-based approach for selection of welding process for aluminum tube manufacturing. Advances in Intelligent Systems and Computing. 2020. Vol. 949. pp. 441–450.
5. Yu E.-L., Xiao Y., Liu F., Li D.-L. et al. Welding and heat treatment of high frequency longitudinal welded pipe. Kang T’ieh. 2019. Vol. 54, No. 6. pp. 1–10.
6. Shevakin Yu. F., Efremov B. N., Pinus L. N., Dozortsev Yu. K. Elimination of brass cracking during high-frequency welding of tubes. Tsvetnye Metally. 1989. No. 12. pp. 81–84.
7. Kozhin V. D., Luzhbina L. Yu., Pevzner M. Z. Prevention of cracking during tube welding at Kirov Non-Ferrous Metals Processing Plant. Tsvetnye Metally. 1990. No. 12. pp. 83–84.
8. Shimov G. V., Shalaeva M. S., Sladkov M. M. Method of definition of residual stresses in copper and brass tubes. Tsvetnye Metally. 2015. No. 11. pp. 80–84.
9. Antimonov A. M., Pushkareva N. B. Line production of cold-deformed brass pipes for car radiators. Tsvetnye Metally. 2019. No. 5. pp. 88–94.
10. GOST 15527–2004. Pressure treated copper zinc alloys (brasses). Grades. Introduced: 01.07.2005.
11. Pevzner M. Z. Analysis of influence of technological factors on crack formation in welding of brass tube. Russian Journal of Non-ferrous Metals. 2005. Vol. 46, No. 4. p. 30.
12. Frame L. D., Davis K., Tupalo O., Ignatowski T., Nallen M. Aspects of precise heat input control for high frequency welding. ASM International – 29th Heat Treating Society Conference, HEAT TREAT 2017. 2017. pp. 524–533.
13. Kawauti Susumu, Tsudzi Masahiro, Yamamoto Mitiaki, Nisikawa Kieaki. Copper alloy for welded tubes. Application 59-126742, Japan. Applied: 07.01.83. Published: 21.07.84.
14. Efimov I. V., Stepanov P. P., Sorokin A. E. Understanding the process of high-frequency tube welding with application of high-speed shooting. Problemy chernoy metallurgii i materialovedeniya. 2020. No. 1. pp. 12–20.
15. Goins P. E., Murdoch H. A., Hernandez-Rivera E., Tschopp M. A. Effect of magnetic fields on microstructure evolution. Сomputational Materials Science. 2018. Vol. 150. pp. 464–474.
16. Nicolay A., Franchet J. M., Cormier J., Loge R. E. et al. Influence of joule effect heating on recrystallization phenomena in inconel 718. Metallurgical and Materials Transactions A: Physical Metallurgy and Materials Science. 2021. Vol. 52, Iss. 10. pp. 4572–4596.
17. Wu Y., Wang Q., Zhao X. Effect of high magnetic field on recrystallization behavior of cold rolled H70 brass. Journal of Physics Conference Series. 14th National Conference on Theory of Magnetism. Hefei, China, 2017. Vol. 827. 012020.
18. Dughiero F., Forzan M., Pozza C., Sieni E. A translational coupled electromagnetic and thermal innovative model for induction welding of tubes. IEEE Transactions on Magnetics. 2012. Vol. 48, No. 2. pp. 483–486.
19. Baake E., Nikanorov A., Ebel W. Numerical modeling of double highfrequency longitudinal welding of cladded pipes. XXI International Conference Complex Systems: Control and Modeling Problems (CSCMP). 2019. pp. 39–42.
20. Efremov B. N., Yushina E. V., Platova S. N., Vasiliev S. D., Lavrentiev M. I. Structural causes of high-temperature decomposition of lead brasses. Izvestiya vuzov. Tsvetnaya metallurgiya. 1988. No. 4. pp. 101–104.
21. Osintsev O. E., Fedorov V. N. Copper and copper alloys. National and foreign grades: reference book. Moscow : Mashinostroenie, 2004. 336 p.
22. GOST 8695–75. Tubing. Flattening testing method. Introduced: 01.07.1977.
23. Kobzar A. I. Applied mathematical statistics. For engineers and research fellows. Moscow : FIZMATLIT, 2012. 816 p.
24. Pevzner M. Z. Process of forming metal alloy band for welding tubes. Patent RF, No. 2290271. Applied: 16.06.2004. Published: 10.01.2006.
25. Gorelik S. S., Dobatkin S. V., Kaputkina L. M. Recrystallization of metals and alloys: 3rd edition. Moscow : MISIS, 2005. 432 p.
26. Pevzner M. Z., Sergeev D. G. Effect of impurities on the properties of brass L63 and preventive control of commercial batches of continuously annealed ribbon at the Kirov plant for processing nonferrous metals. Metal Science and Heat Treatment. 2021. Vol. 63, No. 1-2. pp. 53–59.
27. Wang Y., Wu J., Liu C., Chen L. Simulation and analysis of eddy current field and temperature field of strips during transverse flux continuous induction heating. Heat Treatment of Metals. 2019. Vol. 44, Iss. 1. pp. 229–234.
28. Pevzner M. Z., Shirokov N. M., Khayutin S. G. Continuous induction heat treatment of bands and strips. Moscow : Metallurgiya, 1994. 128 p.
29. Wang X.-P., Wang Z. Multifactorial operation optimization for continuous annealing process based on data analytics. Control and Decision. 2019. Vol. 34, Iss. 12. pp. 2713–2720.
30. Pevzner M. Z. Method for producing L68 alloy bands for high-frequency longitudinal tube welding. Patent RF, No. 2762503. Applied: 09.02.2021. Published: 21.12.2021.

Language of full-text русский
Полный текст статьи Получить
Назад